Standard By:ASTM International, 03/01/2015

Published:2015-03-01

Pages:14

File Size:1 file , 120 KB

Note:This product is unavailable in Russia, Ukraine, Belarus

1.1This specification2 covers seamless ferritic and austenitic steel boiler, superheater, and heat-exchanger tubes, designated Grades T5, TP304, etc. These steels are listed in Tables 1 and 2.

(A)Maximum, unless range or minimum is indicated. Where ellipses (…) appear in this table, there is no requirement, and analysis for the element need not be determined or reported.

(B)It is permissible to order T2 and T12 with a sulfur content of 0.045 max. See 16.3.

(C)Alternatively, in lieu of this ratio minimum, the material shall have a minimum hardness of 275 HV in the hardened condition, defined as after austenitizing and cooling to room temperature but prior to tempering. Hardness testing shall be performed at mid-thickness of the product. Hardness test frequency shall be two samples of product per heat treatment lot and the hardness testing results shall be reported on the material test report.

(A)Maximum, unless a range or minimum is indicated. Where ellipses (…) appear in this table, there is no minimum and analysis for the element need not be determined or reported.

(B)The method of analysis for Nitrogen shall be a matter of agreement between the purchaser and the producer.

(C)For these alloys, there is no common grade designation. The UNS number uniquely identifies these alloys.

(D)For small diameter or thin walls, or both, where many drawing passes are required, a carbon maximum of 0.040% is necessary in Grades TP304L, TP304LN, TP316L, and TP316LN.

(E)Grade S30434 shall have (Ti + ¹/₂Nb) of not less than 2 times and not more than 4 times the carbon content.

(F)Grade TP347LN shall have an Nb content of not less than 15 times the carbon content.

(G)Grade TP348 shall have an Nb + Ta content of not less than 10 times the carbon content and not more than 1.10%.

(H)Grade TP348H shall have an Nb + Ta content of not less than 8 times the carbon content and not more than 1.10%.

(I)Iron shall be determined arithmetically by difference of 100 minus the sum of the other specified elements.

(J)(Al + Ti) 0.85-1.20.

(K)Grade TP444 shall have Ni + Cu = 1.00 max.

(L)Grade TP444 shall have Ti + Nb = 0.20 + 4(C + N)-0.80.

(M)N08020 shall have an Nb + Ta content of not less than 8 times the carbon content and not more than 1.00%.

1.2Grades containing the letter, H, in their designation, have requirements different from those of similar grades not containing the letter, H. These different requirements provide higher creep-rupture strength than normally achievable in similar grades without these different requirements.

1.3The tubing sizes and thicknesses usually furnished to this specification are ¹/₈in. [3.2 mm] in inside diameter to 5 in. [127 mm] in outside diameter and 0.015 to 0.500 in. [0.4 to 12.7 mm], inclusive, in minimum wall thickness or, if specified in the order, average wall thickness. Tubing having other diameters may be furnished, provided such tubes comply with all other requirements of this specification.

1.4The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order.

ASTM A213/A213M-15